Environmental effects on the strength and impact damage resistance of alumina based oxide/oxide ceramic matrix composites

In this study the effects of high temperature and moisture on the impact damage resistance and mechanical strength of Nextel 610/alumina silicate ceramic matrix composites were experimentally evaluated. Composite laminates were exposed to either a 1050°C isothermal furnace-based environment for 30 consecutive days at 6 h a day, or 95% relative humidity environment for 13 consecutive days at 67°C. Low velocity impact, tensile and short beam strength tests were performed on both ambient and environmentally conditioned laminates and damage was characterized using a combination of non-destructive and destructive techniques. High temperature and humidity environmental exposure adversely affected the impact resistance of the composite laminates. For all the environments, planar internal damage area was greater than the back side dent area, which in turn was greater than the impactor side dent area. Evidence of environmental embrittlement through a stiffer tensile response was noted for the high temperature exposed laminates while the short beam strength tests showed greater propensity for interlaminar shear failure in the moisture exposed laminates. Destructive evaluations exposed larger, more pronounced delaminations in the environmentally conditioned laminates in comparison to the ambient ones. External damage metrics of the impactor side dent depth and area directly influenced the post-impact tensile strength of the laminates while no such trend between internal damage area and residual strength could be ascertained.     

Tuning of shear thickening behavior and elastic strength of polyvinylidene fluoride via doping of ZnO-graphene

ZnO rice like nonarchitects are grafted on the graphene carbon core via a rapid microwave synthesis route. The prepared grafted systems are characterized via XRD, SEM, RAMAN, and XPS to examined the structural and morphological parameters. Zinc oxide grafted graphene sheets (ZnO-G) are further doped in β-phase of polyvinylidene fluoride (PVDF) to prepare the polymer nanocomposites (PNCs) via mixed solvent approach (THF/DMF). β-phase confirmation of PVDF PNCs is done by FTIR studies. It is observed that ZnO-G filler enhances the β-phase content in the PNCs. Non-doped PVDF and PNCs are further studied for rheological behavior under the shear rate of 1–100 s⁻¹. Doping of ZnO-G dopant to the PVDF matrix changes its discontinuous shear thickening (DST) behavior to continues shear thickening behavior (CST). Hydrocluster formation and their interaction with the dopant could be the reason for this striking DST to CST behavioral change. Strain amplitude sweep (10⁻³% -10%) oscillatory test reveals that the PNCs shows extended linear viscoelastic region with high elastic modulus and lower viscous modulus. Effective shear thickening behavior and strong elastic strength of these PNCs present their candidature for various fields including mechanical and soft body armor applications.     

巨型水轮发电机剪断销研发与质量控制

为获得设计需要的巨型水轮发电机剪断销的剪切力,得到剪切力波动受控的批量剪断销,通过拉伸试验、冲击试验、硬度试验和剪断销剪切试验等讨论了全尺寸剪断销剪切试验的可行性,分析了剪切试验时正常剪断和非正常剪断的剪断销材料性能差异,探究了剪断销的剪切力质量稳定性控制方法。结果表明:控制剪断销料坯的布氏硬度波动,可实现间接控制剪断销剪切强度的波动;通过试验总结的六步法可达到控制批量剪断销质量和剪切力波动的目的。     

Use of CFD-DEM to evaluate the effect of intermediate stress ratio on the undrained behaviour of granular materials

This study investigates the effect of intermediate stress ratio (b) on the mechanical behaviour of granular soil in true triaxial tests. A CFD-DEM solver with the ability to model compressible fluid and moving mesh has been developed and calibrated based on existing experimental test results on Nevada sand. The effect of b on the undrained true triaxial test, which has been neglected in the literature, was investigated using a reasonable number of models. The effects of the initial confining stress and initial void ratio also have been studied. The developed model was used to calculate the hydrodynamic forces on the particles and evaluate the ratio of the particle–fluid interaction force to the resultant force on the particles. It has been demonstrated that, in numerical studies, the effect of these forces cannot be neglected.     

内含实体对H型垂直轴风力机气动性能的影响

以H型垂直轴风力机及其内含圆柱形实体为研究对象,对NACA0018翼型的五叶片H型垂直轴风力机的气动性能进行数值模拟和实验验证。分析8种不同直径的内含圆柱体,在内含实体截面积占风轮迎风面积之比分别为21.2%、50.0%和76.9%时,风力机风能利用率的峰值分别下降8.04%、20.7%及74.3%。结果表明：随着内含实体直径的增大,风能利用率的峰值逐渐减小,开始较为缓慢,达到一定值时快速下降。小直径内含实体主要影响叶片在下风区的转矩,对风能利用率的影响较小,而大直径内含实体还会影响叶片在上风区的转矩,其风能利用率迅速减小。对于内含固定直径的实体,比如在现有建筑物外侧安装风力机时,其风轮半径的选择需综合考虑风能利用率和风力机的建造成本两方面的因素。研究结果可为建筑物与垂直轴风力机进行有效结合以提高风能的利用提供参考。     

基准平面垂直断面法在爆破漏斗试验中的应用

系统阐述了基准平面垂直断面法在爆破漏斗试验中测量爆破漏斗体积的基本原理,并将隧道激光断面仪应用于金厂河矿1 750 m水平15^#采场底部切割巷道爆破漏斗试验爆破漏斗体积测量中。通过与传统体重法等计算法所得漏斗体积分析比较,结果表明基于隧道激光断面仪与3D Mine软件分析的基准平面垂直断面法实用性强、操作方便、结果直观可靠,达到试验预期目的。     

高面板坝全寿命周期变形控制方法及应用

高面板坝的变形对面板的安全运行有着特别重要的影响，国内外已建的高面板坝工程中，因坝体变形大导致防渗面板挤压破损，坝体渗漏量大的实例较多，不得不降低水库水位进行修复处理，造成较大的经济损失乃至给大坝的长期运行留下安全隐患。通过发生挤压破损的实例分析，发现变形控制缺乏系统性是发生面板挤压破损的主要因素，为预防面板破损，系统提出了“控制坝体总变形，转化有害变形，适应纵向变形”的坝体变形控制方法，并在使用软硬岩混合料筑坝的董箐面板堆石坝中得到的应用，取得了良好效果，该工程运行至今达十余年，未见面板有挤压破损迹象，该方法对建设200 m以上乃至300 m级超高面板坝具有重要借鉴意义。     

印刷电路板缺陷检测的实际应用

电路板在我们的日常生活中非常常见,这就使得印刷电路板的缺陷检测显得尤为重要。AOI作为新兴的检测PCB板缺陷的系统,在生产实际中正在被大家熟知并且应用。相较于传统的检测方式,AOI系统比较灵活,无论是在检测时间还是系统运算上,或者是对相关技术人员的要求相较于传统方式都比较有优势,本文就AOI系统在实际中的应用展开讨论,分析并且介绍了在实际应用中的具体细则。     

"不知火"柑橘全自动包装生产线的设计与研究

目的为了解决柑橘在实际包装过程中因于人工手动装袋、装箱等导致的效率低下问题,设计一条全自动柑橘包装生产线。方法基于“不知火”柑橘的特殊体型特征,使用传送带分级装置对其进行分级;通过倾斜皮带解决柑橘排列姿态的整理问题;经给袋式包装机装袋后,采用扭结式扎口装置对其进行封口;利用并联机器人对其进行装箱。通过计算生产节拍,合理规划每个工序的循环时间,并通过Flexsim软件对该生产线进行仿真分析与平衡优化。结果该生产线整体效率由89%提升到93%,能够正常运行且满足生产力的需求。结论该柑橘包装生产线实现了柑橘的分级、整料、装袋、装箱等工序,降低了工作强度,提高了生产效率,实现了包装过程的自动化。